En10216-2 P195gh, P235gh, P265gh Seamless Steel Tube for Pressure Purpose

• Customization: Available
• Type: Seamless
• Technique: Cold Drawn
• Model NO.: EM-EN10216
• Surface Treatment: Black
• Usage: Pipeline Transport, Boiler Pipe, Hydraulic/Automobile Pipe, Oil/Gas Drilling, Machinery Industry, Chemical Industry, Mining
• Section Shape: Round
• Thickness: 1.2-9.5mm
• Od: 1/2" - 24"
• Transport Package: in Bundles
• Specification: 1/2" - 24"
• Trademark: KINGMETAL
• Origin: China
• Production Capacity: 100000 Ton/ Year

Product Description

EN10216-2 P235GH P265GH Carbon steel pipe
Standard:EN 10216-2
Materials: P235GH,P265GH,P355GH
Technique:cold drawn,hot-rolled
Usage: boiler mill
Length :   double randon length
Thickness:    3-40mm
Outer Diameter:    21-508mm

P235GH/P265GH/P355GH areEuropean specified steel for use in pressure vessels, boilers and heat exchangers. 
The composition of this steel makes it ideal for applications where elevated working temperatures are the norm and the material is used by fabricators throughout the oil, gas and petrochemical industry. 

Chemical Composition of EN P235GH

Element	% by mass	Element	% by mass
Carbon (C)	≤0.16	Silicon (Si)	≤0.35
Manganese (Mn)	0.60 to 1.20	Phosphorous (P) (max)	0.025
Sulphur (S) (max)	0.015	Aluminium (Al)	≤0.020
Nitrogen (N)	≤0.012	Chromium (Cr)	≤0.30
Copper (Cu)	≤0.30	Molybdenum (Mo)	≤0.08
Niobium (Nb)	≤0.020	Nickel (Ni)	≤0.30
Titanium (Ti) (max)	0.03	Vanadium (Vi)	≤0.02

The combined quantities of Chromium, Copper and Molybdenum should not exceed 0.70% 

Table 2: Mechanical Properties of P235GH

Grade	Type	Thickness (mm)	Yield Strength MPa (min)	Tensile Strength MPa	Elongation % (min)	Impact Energy (KV J) (min)
						-20°	0°	+20°
P235GH	Normalized	≤ 16 16> to ≤40 40> to ≤60 60> to ≤100 100> to ≤150 150> to ≤250	235 225 215 200 185 170	360 to 480 360 to 480 360 to 480 360 to 480 350 to 480 350 to 480	24 24 24 24 24 24	27 27 27 27 27 27	34 34 34 34 34 34	40 40 40 40 40 40

Chemical Composition of P265GH

Element	% by mass	Element	% by mass
Carbon (C)	≤0.20	Silicon (Si)	≤0.40
Manganese (Mn)	0.80 to 1.40	Phosphorous (P) (max)	0.025
Sulphur (S) (max)	0.015	Aluminium (Al)	≤0.020
Nitrogen (N)	≤0.012	Chromium (Cr)	≤0.30
Copper (Cu)	≤0.30	Molybdenum (Mo)	≤0.08
Niobium (Nb)	≤0.020	Nickel (Ni)	≤0.30
Titanium (Ti) (max)	0.03	Vanadium (Vi)	≤0.02

The combined quantities of Chromium, Copper and Molybdenum should not exceed 0.70% 

Table 2: Mechanical Properties of EN P265GH

Grade	Type	Thickness (mm)	Yield Strength MPa (min)	Tensile Strength MPa	Elongation % (min)	Impact Energy (KV J) (min)
						-20°	0°	+20°
P265GH	Normalized	≤ 16 16> to ≤40 40> to ≤60 60> to ≤100 100> to ≤150 150> to ≤250	265 255 245 215 200 185	410 to 530 410 to 530 410 to 530 410 to 530 400 to 530 390 to 530	22 22 22 22 22 22	27 27 27 27 27 27	34 34 34 34 34 34	40 40 40 40 40 40

Chemical Composition of P355GH

Element	% by mass	Element	% by mass
Carbon (C)	0.10 to 0.22	Silicon (Si)	≤0.60
Manganese (Mn)	1.10 to 1.70	Phosphorous (P) (max)	0.025
Sulphur (S) (max)	0.015	Aluminium (Al)	≤0.020
Nitrogen (N)	≤0.012	Chromium (Cr)	≤0.30
Copper (Cu)	≤0.30	Molybdenum (Mo)	≤0.08
Niobium (Nb)	≤0.020	Nickel (Ni)	≤0.30
Titanium (Ti) (max)	0.03	Vanadium (Vi)	≤0.02

The combined quantities of Chromium, Copper and Molybdenum should not exceed 0.70% 

Table 2: Mechanical Properties of P355GH

Grade	Type	Thickness (mm)	Yield Strength MPa (min)	Tensile Strength MPa	Elongation % (min)	Impact Energy (KV J) (min)
						-20°	0°	+20°
P355GH	Normalized	≤ 16 16> to ≤40 40> to ≤60 60> to ≤100 100> to ≤150 150> to ≤250	355 345 335 315 295 280	510 to 650 510 to 650 460 to 580 490 to 630 480 to 630 470 to 630	20 20 20 20 20 20	27 27 27 27 27 27	34 34 34 34 34 34	40 40 40 40 40 40