S235 S275 S355 Hot Rolled Steel Coils

• Customization: Available
• Standard: ASTM, JIS, GB, AISI, DIN, BS
• Certification: ISO, IBR
• Model NO.: KM-20210113
• Surface Treatment: Galvanized
• Technique: Hot Rolled
• Application: Jaws of Crushers, Hammers or Pulverizers,etc
• Edge: Slit edge
• Stock: Not Stock
• Transport Package: According to Seaworthy Export Package.
• Specification: Width: 30~1000mm, Thickness: 1~10mm, Length: Coils
• Trademark: Kingmetal
• Origin: Made in China
• HS Code: 7208261000
• Production Capacity: 10000 Tons Per Month

Product Description

S235 S275 S355 Hot Rolled Steel Coils

 

Description:

In most metals but not all, plate generally starts at 0.188″ (3/16″) thick. Due to its thickness, plate is often used for structural applications such as heavy equipment manufacturing, bridge and building erection.

Plate is measured in inches and not gauges, like sheet product.

Plate is available in Hot Rolled, Aluminum, Stainless Steel and more. It can be purchased online and at any Metal Supermarkets location. It can be cut to your exact specifications.

 

Hot rolling is a mill process which involves rolling the steel at a high temperature (typically at a temperature over 1700° F), which is above the steel's recrystallization temperature. When steel is above the recrystallization temperature, it can be shaped and formed easily, and the steel can be made in much larger sizes. Hot rolled steel is typically cheaper than cold rolled steel due to the fact that it is often manufactured without any delays in the process, and therefore the reheating of the steel is not required (as it is with cold rolled). When the steel cools off it will shrink slightly thus giving less control on the size and shape of the finished product when compared to cold rolled.

 

Specification:

Standard	Grade	C max	Mn max	Si max	P	S	N	Cu	Yield strength max	Tensile strength	Elongation%
EN10025	S235JR	0.22	1.50	---	0.045	0.045	0.014	0.60	175Mpa	340-510 Mpa	17
EN10025	S235J0	0.19	1.50	---	0.040	0.040	0.014	0.60	175Mpa	340-510 Mpa	19
EN10025	S235J2	0.19	1.50	---	0.035	0.035	0.014	0.60	165Mpa	340-510 Mpa	19
EN10025	S275JR	0.25	1.60	---	0.045	0.045	0.014	0.60	205Mpa	330-510	19
EN10025	S275J0	0.21	1.60	---	0.040	0.040	0.014	0.60	205	380-540	19
EN10025	S275J2	0.21	1.60	---	0.035	0.035	---	0.60	195	380-540	19
EN10025	S355JR	0.27	1.70	0.60	0.045	0.045	0.014	0.60	275	450-680	22
EN10025	S355J0	0.24	1.70	0.60	0.045	0.045	0.014	0.60	265	450-680	22
EN10025	S355J2	0.22	1.70	0.55	0.045	0.045	0.014	0.60	255	450-680	22

 

Material	S235,S275,S355
Thickness	1mm-10mm
Width	30mm-1000mm
Length	Coils
Delivery condition	Hot rolled, controlled rolled, or normalized
Cutting service	Large steel plate cut to flat plate sizes, or cut to any size by drawing
Deep processing	After cutting large plate into the general sizes by drawing, milling and grinding, and make angles, polishing, and make special parts

 

Application:

Hot rolled steel plate  is the ideal solution for cases where severe wear is combined with shocks or high pressure capable of work-hardened its austenitic structure. Used in jaws of crushers, hammers or pulverizers, cutting edges of large excavators, liners of shotblasting units, cores and wall of parpen moulds, and screens.

 

Our service:

1. 24 hours on line and prompt reply;

2. Free sample offered;

3. Flexible payment term with L/C at sight,TT ,ect;

4. Big quantity supply and short delivery time;

5. Long period after-sale service.

 

We are professional and international:

We have many experienced employees. Among those, some are professional staffs who have worked in the international steel field for over 30 years. With excellent team-work, we know well about how to handle iron and steel international business with professional service which has brought our continuous business growth .and our customer's satisfaction from the beginning.