1.2080 Rods Cold Work Tool Steel X210cr12 Bar

• Customization: Available
• Type: Alloy Steel Bar
• Standard: AISI, ASTM, GB, JIS, DIN, BS
• Model NO.: MD-810
• Technique: Forged
• Application: Tool Steel Bar
• Surface Treatment: Peeled
• Alloy: Alloy
• Special Use: Tool Steel
• Size: 16mm-1000mm
• Length: 2m,3m,5.8m, 6m, 8m or as Required.
• Delivery Time: 7-30 Days
• Loading Port: Shanghai
• MOQ: 1 Tons
• Certificate: ISO, BV, SGS, Mill Test Certificate
• Packaging Detail: Standard Sea-Worthy Package
• Surface: Peeled, Polish
• Price Term: Ex-Work, Fob, CFR, CIF, etc.
• Specifications: Flat Bar, Round Bar, Angle Bar, Square Bar
• Transport Package: Standard Sea-Worthy Package
• Specification: 16mm-1000mm
• Trademark: Kingmetal
• Origin: China (Mainland)
• Production Capacity: 800tons/Month

Product Description

DIN 1.2080 Tool Steel | X210Cr12 | AISI D3 | SKD11
 

DIN 1.2080 steel contains 2.1% carbon and more than 11% chromium alloy, which is defined as high carbon and high chromium cold work tool steel as per DIN 17350 standard.

As one of the classic representative steels of cold work tool steel, DIN 1.2080 steel has the characteristics of high strength, high toughness, high hardness, high hardenability, excellent wear resistance and good processing performance.

DIN 1.2080/X210Cr12 steel  is usually delivered in annealed condition with hardness below 248HBW.
 

DIN 1.2080/X210Cr12 STEEL CHEMICAL COMPOSITION

Grade	C	Si	Mn	P	S	Cr
1.2080	1.9-2.2	0.1-0.4	0.15-0.45	≤0.03	≤0.03	11.0-12.0

DIN 1.2080/X210Cr12 STEEL  RELATED STANDARD & EQUIVALENT GRADE

China:Cr12

USA:D3

Japan:SKD11

DIN 1.2080/X210Cr12 STEEL FORGING

• Initial Forging Temperature:1080-1100ºC
• Final Forging Temperature:880-920ºC
• Forging Ratio:above 4:1
• Cooling Method After Forged:As high carbon-chromium cold work tool steel ,DIN 1.2080 steel should be annealed after forging.

DIN 1.2080/X210Cr12 STEEL HEAT TREATMENT

Critical Temperature for Heat Treatment of  DIN 1.2080 Steel

• Ac1:810ºC
• Ac3:835ºC
• Ar1:755ºC
• Ms:180ºC

DIN 1.2080 steel Annealing

The general annealing temperature of DIN 1.2080 steel is 850-870ºC,and the holding time is 3-6 hours,and then furnace cooled to 500-600ºC with the rate 30ºC/h max.Annealed hardness is usually below 248HBW.

DIN 1.2080 Steel Annealing 

DIN 1.2080 steel Quenching & Tempering

Pre-heat Temperature:800-850ºC

Quenching Temperature:950-980ºC

Quenching Medium:oil

Tempering Temperature:180-200ºC Followed by Quenching

Hardness: 60-62HRC

DIN 1.2080 Steel Tempering VS Hardness 

 

 

DIN 1.2080/X210Cr12 STEEL SUPPLY FORM & SIZE & TOLERANCE

Hot Forged Round bar:Φ80-Φ1000mm

Hot Rolled  Round bar:Φ16-Φ130mm

Hot Forged Square bar: Max Thickness:500mm

Flat bar/Blcoks:Thickness :120-800mm ,Width:120-1500mm

Surface Finish	Black-Forged	Black-Rolled	Turned	Grinding	Polished	Peeled	Cold Drawn
Tolerance	(0,+5mm)	(0,+1mm)	(0,+3mm)	Best h9	Best h11	Best H11	Best H11

DIN 1.2080/X210Cr12 STEEL APPLICATIONS

Cutting tools, guillotine blades for cutting steel sheet up to about 3 mm thick and for cutting hardened steel strip, broaches, highly stressed woodworking tools where the toughness requirement is not too high, shaping and flanging tools, blades for producing chopped wire, thread rolling tools, deep drawing tools, press tools for the ceramic and pharmaceutical industry,drawing cones for wire drawing, extruding tools and guide strips, sand blasting nozzles.