Hastelloy C4 Alloy Seamless Tubing

• Customization: Available
• Type: Alloy Steel Pipe
• Standard: AISI, ASTM, DIN, JIS
• Model NO.: KM-20240328
• Technique: Cold Drawn
• Shape: Bar
• Surface Treatment: Polished
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Heat Exchager Tube,Boiler Tube,Oils&Gas,etc
• Product Standard: ASTM B619 B622 B626 N06645
• Materials: Hastelloy C4 2.4610 Nimo16cr16ti
• Sizes: 6.35-406.4mm, Customized
• Heat Treatment Condition: Solution Annealing and Water Rapid Quenched
• Package: in Bundles, Plywood Cases
• Surface: Pickled,Passivation,Inside & Outside Mechanical Po
• Transport Package: in Bundle or Wooden Box
• Specification: 6~60.3MM
• Trademark: KM
• Origin: Made in China
• HS Code: 75071200
• Production Capacity: 1000 Tons Per Month

Product Description

Hastelloy C4 Alloy Seamless  tubing

HASTELLOY C4 PIPE SPECIFICATION

Steel Grade	N06455, 2.4610	Type	Seamless
Standard	ASTM, AISI, GB, DIN, JIS	Certification	ISO,SGS,BV,ISO/CE/SGS
Length	15000mm Max, Customized	Thickness	0.508-50.8mm
Technique	Cold Rolled, Cold Drawn	Min./Avg.	Avg.
Outer Diameter	6.35-406.4mm, Customized	Finish	Brush Polish Cold Drawn, Pickled,Bright Annealed

Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 alloy is a nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. This alloy resists the formation of grain-boundary precipitates in the weld heat-affected zone, thus making it suitable for most chemical process applications in the as welded condition. C-4 alloy also has excellent resistance to stress-corrosion cracking and to oxidizing atmospheres up to 1900°F (1038°C).

 

Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 alloy has exceptional resistance to wide variety of chemical process environments. These include hot contaminated mineral acids, solvents, chlorine nd chlorine contaminated media (organic and inorganic), dry chlorine, formic acid and acetic acid, acetic anhydride, and seawater and brine solutions.

Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 N06455 alloy can be forged, hot-upset, and impact extruded. Although the alloy tends to work-harden, it can be successfully deep-drawn, spun, press formed or punched. All of the common methods of welding can be used to weld Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 N06455 alloy, although the oxy-acetylene and submerged arc processes are not recommended when the fabricated item is intended for use in corrosion service. Special precautions should be taken to avoid excessive heat input.

Hastelloy C4 Alloy ASTM B619 B622 B626 N06645 Alloy Chemical compostion:

ASTM B622 N06645 Hastelloy C4 Alloy Chemical Composition:

Ni

Mo

Fe

C

Co

Cr

Mn

Si

Ti

W

Al

Cu

V

P

S

Zr

Nb

Ta

Rem.

14.0- 17.0

3.0 max

0.015 max

2.0 max

14.0- 18.0

1.0 max

0.08 max

0.70 max

1.0 max

0.04 max

0.03 max

DIN 17744 2002 2.4610 NiMo16Cr16Ti Hastelloy C4 Alloy Chemical Composition:

Ni

Mo

Fe

C

Co

Cr

Mn

Si

Ti

W

Al

Cu

V

P

S

Zr

Nb

Ta

Rem.

14.0- 17.0

3.0 max

0.015 max

2.0 max

14.0- 18.0

1.0 max

0.08 max

0.70 max

0.50 max

0.025 max

0.015 max