C46400 yellow brass plates
C46400 Naval Brass is classed as naval brass and is a 60% copper 40% zinc with 1% tin alloy. The addition of tin is made for extra corrosion resistance in seawater and other mildly aggressive environments. It also offers good strength levels combined with an excellent hot formability.
C46400 is a good corrosion resistant brass with excellent hot forgeability. Its soldering and brazing capabilities are excellent along with its hot working capacity.
Atlas carries C46400 Diamond Cut Brass Sheet and Plate in a number of thicknesses and widths. We will cut the brass sheets to width and length on one of our precision cut plate saws. C46400 is one of the top choices for industrial and marine atmosphere applications. This is due to it's high corrosion resistance to seawater.
C46400 Naval Brass Sheet has good corrosion resistance, Excellent hot workability, and hot forgeability. Fabricated by blanking, drawing, bending, heading and upsetting, hot forging, pressing.
STANDARD SIZES
Plate - 4.76mm~101.6mm thick, 1000~3000mm width, 2000~6000mm length
Sheet - 0.31mm~2mm thick, 1000~3000mm width, 2000~6000mm length
(Diamond Cut) - ¼" to 1" thick
C46400 DIAMOND CUT SPECIFICATIONS
TYPICAL C46400 CHEMICAL COMPOSITION(%max., unless shown as range or min.) NOTE: Information courtesy kingmetal2009.en.made-in-china.com
|
Cu |
Fe |
Pb |
Zn |
Min./Max. |
68.5-71.5 |
.05 |
.07 |
Rem. |
Nominal |
70.0 |
- |
- |
30.0 |
Note: Cu + Sum of Named Elements, 99.7% min.
TYPICAL C46400 MECHANICAL PROPERTIES(measured at room temperature, 68 F (20 C) NOTE: Information courtesy kingmetal2009.en.made-in-china.com
Temper |
Section
Size |
Cold
Work |
Typ/
Min |
Temp |
Tensile
Strength |
Yield
Strength
(0.5% ext.
under load) |
Yield
Strength
(0.2%
offset) |
Yield
Strength
(0.05%
offset) |
El |
Rockwell
Hardness |
Vickens
Hard. |
Brinell
Hard. |
Shear
Strength |
Fatigue
Strength* |
Izod
Impact
Strength |
|
in. |
% |
|
F |
ksi |
ksi |
ksi |
ksi |
% |
B |
C |
F |
30T |
500 |
500 |
3000 |
ksi |
ksi |
ft-lb |
|
mm. |
|
|
C |
MPa |
MPa |
MPa |
MPa |
|
|
|
|
|
|
|
|
MPa |
MPa |
J |
Tube |
H80 |
0.0 |
35 |
TYP |
68 |
78 |
64 |
- |
- |
8 |
82 |
- |
- |
73 |
- |
- |
- |
- |
- |
0.0 |
|
0.0 |
|
|
20 |
538 |
441 |
- |
- |
8 |
82 |
- |
- |
73 |
- |
- |
- |
- |
- |
0.0 |
Flat Products |
OS015 |
0.04 |
0 |
TYP |
68 |
53 |
22 |
- |
- |
54 |
- |
- |
78 |
43 |
- |
- |
- |
35 |
14 |
0.0 |
|
1 |
|
|
20 |
365 |
152 |
- |
- |
54 |
- |
- |
78 |
43 |
- |
- |
- |
241 |
97 |
0.0 |
H02 |
0.04 |
0 |
TYP |
68 |
62 |
52 |
- |
- |
25 |
70 |
- |
- |
65 |
- |
- |
- |
40 |
18 |
0.0 |
|
1 |
|
|
20 |
427 |
359 |
- |
- |
25 |
70 |
- |
- |
65 |
- |
- |
- |
276 |
124 |
0.0 |
Flat Products |
H06 |
0.04 |
0 |
TYP |
68 |
86 |
65 |
- |
- |
5 |
88 |
- |
- |
76 |
- |
- |
- |
46 |
- |
0.0 |
|
1 |
|
|
20 |
593 |
448 |
- |
- |
5 |
88 |
- |
- |
76 |
- |
- |
- |
317 |
- |
0.0 |
OS100 |
0.04 |
0 |
TYP |
68 |
44 |
11 |
- |
- |
66 |
- |
- |
54 |
11 |
- |
- |
- |
- |
13 |
0.0 |
|
1 |
|
|
20 |
303 |
76 |
- |
- |
66 |
- |
- |
54 |
11 |
- |
- |
- |
- |
90 |
0.0 |
OS035 |
0.04 |
0 |
TYP |
68 |
49 |
17 |
- |
- |
57 |
- |
- |
68 |
31 |
- |
- |
- |
34 |
14 |
0.0 |
|
1 |
|
|
20 |
338 |
117 |
- |
- |
57 |
- |
- |
68 |
31 |
- |
- |
- |
234 |
97 |
0.0 |
H04 |
0.04 |
0 |
TYP |
68 |
76 |
63 |
- |
- |
8 |
82 |
- |
- |
73 |
- |
- |
- |
44 |
21 |
0.0 |
|
1 |
|
|
20 |
524 |
434 |
- |
- |
8 |
82 |
- |
- |
73 |
- |
- |
- |
303 |
145 |
0.0 |
Flat Products |
H08 |
0.04 |
0 |
TYP |
68 |
94 |
65 |
- |
- |
3 |
91 |
- |
- |
77 |
- |
- |
- |
48 |
23 |
0.0 |
|
1 |
|
|
|
|
|
Product |
Specification |
Bar |
ASTM B36, B19 |
SAE J463, J461 |
Brazing Filler Metal |
FEDERAL QQ-B-650 |
Cups, Cartridge Case |
ASTM B129 |
MILITARY MIL-C-10375 |
Disk |
ASTM B19 |
Plate |
AMS 4507, 4505 |
ASTM B19, B36 |
Rod |
SAE J461, J463 |
Sheet |
AMS 4507, 4508, 4505 |
ASTM B19, B36 |
SAE J463, J461 |
Shim Stock, Laminated |
MILITARY MIL-S-22499 |
Strip |
AMS 4507, 4505 |
ASTM B36, B569, B19, B888 |
SAE J463, J461 |
Tube, Seamless |
ASTM B135 |
FEDERAL WW-T-791 |
MILITARY MIL-T-20219 |
SAE J461, J463 |
Tube, Welded |
ASTM B587, B587 |