Hastelloy Nickel-Chromium-Iron-Molybdenum Round Bar

• After-sales Service: Change/Return
• Warranty: 10 Year, 10 Year
• Type: Alloy Steel Bar, Alloy Steel Bar
• Standard: AISI, ASTM, ASTM
• Technique: Hot Rolled, Hot Rolled
• Alloy: Alloy, Alloy
• Application: Structural Steel Bar
• After-Sales Service: Change
• Surface: Bright, Black
• Density: 9.24 g/cm3
• Melting Range: 1330-1380ºC
• Standard or Not: Standard
• Payment: L/C, T/T
• Brand: Kingmetal
• Secondary or Not: Non Secondary
• Transport Package: in Bundle, Wooden Case, or as Request
• Specification: 10-150mm
• Trademark: kingmetal
• Origin: China
• HS Code: 722870
• Production Capacity: 60 Ton/Month

Product Description

Hastelloy Nickel-chromium-iron-molybdenum Round Bar 

Product Introduction

Hastelloy X is a solid-solution-strengthened nickel-chromium-iron-molybdenum alloy that combines good oxidation resistance, high-temperature strength and exceptional stress-corrosion resistance which makes this alloy also interesting for petrochemical applications. Therefore, Hastelloy X was also the material selected for metal injection molded fuel nozzle applications (Fribourg & Castagne, 2014). Metal injection molded HX was also investigated by Wohlfromm et al. (2003) using a HX powder with particle size < 22 μm. Via sintering at 1300°C for 3 h under hydrogen atmosphere a relative density of 97.8% could be achieved. An additional HIP treatment (1185°C/100 MPa/4 h) led to 100% densification. The tensile properties in the solution-annealed state were better than that of a cast alloy, but lower compared to wrought reference material.

Equivalent designations
UNS N10675
DIN W. Nr. 2.4600

Form	ASTM
Rod	B 335
Plate, sheet and strip	B 333, B 906
Seamless pipe and tube	B 622
Welded pipe	B 619, B 775
Welded tube	B 626, B 751
Welding fitting	B 366

Chemical composition

%	Ni	Mo	Fe	Co	Cr	C	Mn	Si	P	S	V
min	balance	26.0	4.0								0.20
max		30.0	6.0	2.5	1.00	0.050	1.00	1.00	0.040	0.030	0.40

Physical properties

Density	9.24 g/cm3
Melting range	1330-1380ºC