AISI H12 1.2605 X35crwmov5 Hot Work Tool Steel

• Customization: Available
• Type: Alloy Steel Bar
• Standard: AISI, ASTM, GB, JIS, DIN, BS
• Model NO.: KM-20240730
• Technique: Hot Rolled
• Application: Structural Steel Bar, Tool Steel Bar, Die Steel Bar
• Surface Treatment: Coated
• Alloy: Alloy
• Special Use: Mold Steel, Free Cutting Steel, Cold Heading Steel, Tool Steel
• Size: 5-900mm
• Delivery Time: 15-30 Days After Down Payment
• Secondary or Not: Non Secondary
• Surface: Pickled,Black,Bright,Polishing,etc
• Processing Method: Hot Work or Cold Drawn
• Packaging: in Bundles or Wooden Boxes
• Transport Package: in Bundle
• Specification: ASTM, JIS, En, DIN, GB, Ks
• Trademark: kingmetal
• Origin: China
• HS Code: 730723
• Production Capacity: 5000 Ton/Month

Product Description

AISI H12 1.2605 X35CrWMoV5 Hot Work Tool Steel

Hot-work steels contain chromium, tungsten and molybdenum. Their properties are matched specifically to high-temperature applications.They are used for hot-work tools, die casting tools, extrusion tools.Pressures die casting and extrusion, the ultimate test of a hot work tool steel. Only very special steels are suited to these applications. Typical applications for hot work tool steels are: pressure dies casting, hot extrusion, open die forging, and plastic processing.

AISI h12 tool steel is a 4.75~5.5% chromium, general-purpose hot work steel. H12 tool steel contains (0.2~0.5%) less vanadium than the widely-used H13 hot works tool steel (0.8~1.2%). 

Grade :	X35CrWMoV5
Number:	1.2605
Classification:	Hot-work tool steel
Standard:	EN ISO 4957: 2000 Tool steels

 

H12 Tool Steel and Equivalent Chemical Composition

ASTM A681	C		Mn		P	S	Si		Cr		V		W		Mo		Ni	Cu	Sn
H12/T20812	0.30	0.40	0.20	0.60	0.03	0.03	0.80	1.25	4.75	5.50	0.20	0.50	1.00	1.70	1.25	1.75	…	…	…
DIN ISO 4957	C		Mn		P	S	Si		Cr		V		W		Mo
1.2605/X35CrWMoV5	0.32	0.40	0.20	0.50	0.03	0.02	0.80	1.20	4.75	5.50	0.20	0.50	1.10	1.60	1.25	1.60	…	…	…
JIS G4404	C		Mn		P	S	Si		Cr		V		W		Mo
SKD62	0.32	0.40	0.20	0.50	0.03	0.02	0.80	1.20	4.50	5.50	0.20	0.50	1.00	1.60	1.00	1.60	…	…	…
BS 4659	C		Mn		P	S	Si		Cr		V		W		Mo
BH12	0.30	0.40	…	0.40	0.35	0.35	0.85	1.15	4.75	5.25	…	0.50	1.25	1.75	1.25	1.75	0.40	0

 

AISI H12 Tool Steels Standard and Relevant Steel Specifications

Country	USA	German	Japan	British
Standard	ASTM A681	DIN EN ISO 4957	JIS G4404	BS 4659
Grades	H12/T20812	1.2605/X35CrWMoV5	SKD62	BH12

 


For hot works tool steels application, we could supply some common tool steels, like H10 steel, H11 steel and H13 steel, and we could also supply AISI h12 tool steel materials for your hot works applications.
 
ASTM/AISI H12 Steel is a deep-hardening, air-hardening steel that exhibits minimal size change during heat treatmnet. H12 tool steel material has good resistance to thermal fatique cracking (heat cracking) and excellent resistnce to gross cracking and thermal shock when water cooled in service. So, we could say H-12 tool steel mainly has the following characteristics:
Excellent resistance to wear, high strength at elevated temperature.
Good homogenizing with high toughness.
Extra- fine- structure without grain-boundary carbide.
Inclusion shape controlled with high cleanliness.
 

ASTM H12 Tool Steel Supply Range

H-12 Steels Bar: diameter 8mm-1000mm
H12 Steel Flat: thickness 16-500mm x width 200-800mm
H12 Steels Plate: thickness 16-500mm x width 200-810mm
Other dimension according to your requirements
 
Surface Finish: Black, Rough Machined, Peeled, Turned or as per given requirements.
 

H12 Hot Work Tool Steel Mechanical Properties

Modulus of elasticity [103 x N/mm2]: 207
Density [g/cm3]: 7.84
Thermal conductivity [W/m.K]: 18.9
Coefficient of Linear Thermal Expansion 10-6 oC-1

20-100oC	20-200oC	20-400oC	20-600oC
9.8	11	12.1	13

 
Forging of H12 Tool Steel
Hot forming temperature: 1100-850oC.
 

H12 Tool Steel Heat Treatment

Annealing
Heating Steel H-12 slowly and uniformly to 845~900ºC, furnace cooling to 540ºC at a rate 10~20ºC/hr. Hardness HB 229 max
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating H12 steel to approx.650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Preheating (1): Heat H-12 steel to approx. 540~650ºC, holding 30 minutes per 25mm.
Preheating (2): Heat H12 tool steels to approx. 845~870ºC, holding 30 minutes per 25mm.
Austenitizing: Heat steel H12 to approx. 1010~1050ºC, holding 30 minutes per 25 mm.
Quenchant: By oil or air.
Tempering
Tempering temperature: 520-700oC, hold at least 2 hours, air cooling and double tempering.
 

Applications of AISI H12 Tool Steel

AISI H12 hot work tool steel is usually used for hot tooling applications where maximum resistance to cracking is required. Such typical applications include the following:
Extrusion indushry: dies and inner liner for extrusion, extrusion tools
Forging Industry: forming dies, press dies
Die casting industry: dies for die-carbide
Tool Industry: hot punch, hot shear blades, immediate roller for cold rolling
 
The material X35CrWMoV5 with the standard DIN/EN is also available with at least 3 alternative names, such as eg: DIN/EN: "X35CrWMoV5" and BSI/AFNOR: "T20812" and AISI/SAE: "H12".
The norm of steel material X35CrWMoV5 is EN ISO 4957