DIN 1.3343 AISI M2 High Speed Steel Bars

• Customization: Available
• Type: Alloy Steel Bar
• Standard: AISI, ASTM, DIN
• Model NO.: KM-20230316
• Application: Tool Steel Bar, Die Steel Bar
• Surface Treatment: Black/Turning/Grinding
• Alloy: Alloy
• Special Use: Mold Steel, Tool Steel
• Related Specification: M2, Skh51/Skh9, T11302, P6m5
• Standards: ISO 4957, DIN 17350.
• Techniques: Cold Drawn; Hot Rolled; Cold Rolled; Forged
• Transport Package: in Bundles or Wooden Boxes.
• Specification: 10mm~300mm
• Trademark: KINGMETAL
• Origin: China
• HS Code: 7228100000
• Production Capacity: 1000 Tons Per Month

Product Description

DIN 1.3343 AISI M2 High Speed Steel Bars

DIN 1.3343 AISI M2 High Speed Steel Bars is the most utilized high-speed steel in the marketplace. It is characterized by high hot wear resistance and has good toughness even in the hardened state. The M2 was originally developed for cutting tools such as turning tools, drills, milling cutters and broaches. However, nowadays it is also widely used for cold work such as punches, thread rolling dies and rolls, and knives.
 

teel Grade	1.3343 / M2	Application	Tool steel, Mold Steel
Shape	Round Bar	Standard	GB, ASTM, DIN,JIS
Dimension	Φ10-300 mm; length below 12m	Surface	Black, Bright, Polished, Peeled
Technique	Cold drawn; Hot rolled; Forged	Ultrasonic Test	100% UT Passed

 

DELIVERY CONDITIONS

 

	Diameter (mm)
Cold drawn	10-100
Peeled	30-160
Grinded	10-600
Turned	130-1600
Hot Rolled	20-280
Hot Forged	130-1000

 

-EAF+(ESR) or EAF+LF+VD+(ESR)

-HOT rolled or Forged, Annealed

-Surface Finish: Black, Rough Machined, Peeled, Turned or as per given requirements

-UT 100% passed

-Cutting service provided

-Third Party inspection is acceptable (SGS, BV etc.)

 

EQUIVALENT GRADES

 

AISI/SAE	DIN	JIS	GB
M2	1.3343 HS6-5-2C	SKH51	CW6Mo5Cr4V2

 

CHEMICAL COMPOSITION (%)

 

	C	Si	Mn	P	S	Cr	Mo	V	W
M2	0.95 1.05	0.20 0.45	0.15 0.40	≤ 0.030	≤ 0.030	3.75 4.50	4.50 5.50	1.75 2.20	5.50 6.75

 

MECHANICAL PROPERTIES

Mechanical properties	Metric	Imperial
Hardness, Rockwell C (tempered at 1150°F, quenched at 2200°F)	62	62
Hardness, Rockwell C (as hardened, quenched at 2200°F)	65	65
Compressive yield strength (when tempered at 300°F)	3250 MPa	471000 psi
Izod impact unnotched (when tempered at 300°F)	67 J	49.4 ft-lb
Abrasion (loss in mm3, as-hardened; ASTM G65)	25.8	25.8
Abrasion (loss in mm3, tempered at 1275°F; ASTM G65)	77.7	77.7
Poisson's ratio	0.27-0.30	0.27-0.30
Elastic modulus	190-210 GPa	27557-30458 ksi